DW-035 High-speed copper plating bath stable inhibitors

DW-035 High-speed copper plating bath stable inhibitors

 

DW-035 High-speed copper plating bath stable inhibitors
Dw-035 stabilizer is a copper, copper can improve the adhesion of the wire surface. This product helps when plating copper wire attached to the surface, making the process more smoothly after the drawing.
Performance: Wire-speed copper stabilizer Dw-035 is a liquid. Was added at a concentration of 1-2ml / l.
Copper plating solution is concentrated sulfuric acid and copper salts, salts formed stable antioxidant, contains copper sulfate, copper stabilizer may be added to improve the adhesion of copper.
1, craft ratio
Matching criteria:
                 Chemical Name      Range      Optimum
                     Copper sulfate pentahydrate   50-80 g / l     60g / l
                     Sulfuric acid (sp g 1.84)       80-120 g / l   90g / l
                     Dw-035 stabilizer            0.75-1.5 ml / l  1ml / l
Work Values:
Ideal parameters
                 Temperature 30-65 ℃ 45 ℃
                 Time 1-30 seconds 3-10 seconds,
Best of precipitation depend optimum temperature. ,
2, additional methods
Increase the concentration of copper sulfate can remain unchanged. Each added 10 KG of copper sulfate to be added 100-150ml of high-speed copper wire stabilizer Dw-035. Concentrated sulfuric acid control PH value should be less than 2.
3, impurity ferrous sulfate treatment:
In the wire rod per 1 kg of copper precipitated had 0.88 kg of iron ions dissolved in the solution, when the solution concentration of 160-180 g / l when they have to replace the solution. Preferably copper sulfate processing integrated processor. But as long as the practices of iron under normal circumstances will not be exceeded, as a stabilizer was added chelated iron and iron sedimentation substance, which is higher than the E-1 is a clear indicator.
4, a stabilizer
Carbon dioxide gas shielded welding wire for optimum chemical copper stabilizer, the overall performance is higher than the E-1
Can reduce the consumption of copper coating is very uniform and compact
Improve the adhesion of the copper plating, lubricity better when drawing
Reduce the risk of the coating from the skin, the coating is not easy to fall off the drawing process
Reduce spatter, welding stabilizer added antioxidant stabilizer salt, copper layer difficult to change, corrosion
Reduce processing cycle iron ions, iron ions practices should not be exceeded under normal circumstances
Remarks:
The product description is available based on years of experience and practice by giving users recommendations, this product is to be adjusted according to the actual situation on the relevant parameters to achieve the best results; wastewater treatment and safe use of the relevant local regulations should be followed law.